Database of Zeolite Structures
 
Framework Type HEI
Powder Diffraction Pattern for HPM-18, ordered, calcined
Input Parameters
  Wavelength:  or
  2θ range:
  Step size:
  Polarization factor:
  Background:
  Reference peak is
    peak closest to °2θ
    reflection (hkl)
       scaled to
  Intensity axis:
     
Peak shape
  Pseudo-Voigt: (1-n)Gaussian + n Lorentzian
  FWHM = sqrt (U + V tan θ + W tan2θ)
  Mixing parameter (n): %
  Peak range: FWHM
  Peak width:
    set UVW at: U =   V =   W =
    FWHM =
    FWHM =
  FWHM =
   
Select Output
 
List hkl and intensity
List powder pattern
plot powder pattern
Crystal Data
  Space Group: P-1   (# )   
  Cell parameters: a = 20.65955 Å b = 10.29947Å c = 14.6012 Å
    α = 90.2053° β = 109.3576° γ = 104.6631 °
  Chemical Formula [Si40Ge8O96]-HEI
  Refinement: Rietveld refinement, R(wp): 11.52 %, GoF: 1.92
  Reference: Yu, H., Zhang, Z., Li, J., Balestra, S.R.G., Rei Gao, Z. and Camblor, M. A.
Journal of Materials Chemistry A, , (2026)
  Atomic Coordinates:          
   
Atom
Form Factor
x
y
z
PP
B(iso)
    
  Ge1
Ge
0.13427 0.04127 0.99184 0.268 2
  Ge2
Ge
0.92277 0.07989 0.21992 0.48 2
  Ge5
Ge
0.7054 0.08189 0.53499 0.003 2
  Ge6
Ge
0.65711 0.04737 0.30687 0.411 2
  Ge8
Ge
0.29971 0.10747 0.09848 0.341 2
  Ge9
Ge
0.10698 0.02643 0.18698 0.267 2
  Ge10
Ge
0.28304 0.09677 0.29269 0.314 2
  Ge15
Ge
0.66023 0.36896 0.30835 0.298 2
  Ge17
Ge
0.29063 0.60235 0.46866 0.314 2
  Ge18
Ge
0.08119 0.42638 0.77898 0.343 2
  Ge19
Ge
0.13237 0.53502 0.46411 0.279 2
  Ge21
Ge
0.30374 0.42781 0.1049 0.33 2
  Ge22
Ge
0.28792 0.41036 0.30227 0.171 2
  Ge23
Ge
0.53372 0.39594 0.13023 0.222 2
  Si1
Si
0.13427 0.04127 0.99184 0.732 2
  Si2
Si
0.92277 0.07989 0.21992 0.52 2
  Si3
Si
0.13659 0.84159 0.46035 1 2
  Si4
Si
0.01352 0.87282 0.28813 1 2
  Si5
Si
0.7054 0.08189 0.53499 0.997 2
  Si6
Si
0.65711 0.04737 0.30687 0.589 2
  Si7
Si
0.80928 0.12851 0.31273 1 2
  Si8
Si
0.29971 0.10747 0.09848 0.659 2
  Si9
Si
0.10698 0.02643 0.18698 0.733 2
  Si10
Si
0.28304 0.09677 0.29269 0.686 2
  Si11
Si
0.47329 0.09584 0.87415 1 2
  Si12
Si
0.19098 0.5635 0.68642 1 2
  Si13
Si
0.43798 0.09363 0.06417 1 2
  Si14
Si
0.11917 0.33126 0.19745 1 2
  Si15
Si
0.66023 0.36896 0.30835 0.702 2
  Si16
Si
0.14104 0.34942 0.99414 1 2
  Si17
Si
0.29063 0.60235 0.46866 0.686 2
  Si18
Si
0.08119 0.42638 0.77898 0.657 2
  Si19
Si
0.13237 0.53502 0.46411 0.721 2
  Si20
Si
0.02101 0.37892 0.29054 1 2
  Si21
Si
0.30374 0.42781 0.1049 0.67 2
  Si22
Si
0.28792 0.41036 0.30227 0.829 2
  Si23
Si
0.53372 0.39594 0.13023 0.778 2
  Si24
Si
0.43986 0.59059 0.06177 1 2
  O1
O
0.84751 0.07494 0.24338 1 2
  O2
O
0.10037 -0.00297 0.07464 1 2
  O3
O
0.05095 0.89875 0.20867 1 2
  O4
O
0.73094 0.02954 0.29306 1 2
  O5
O
0.8552 0.13159 0.42701 1 2
  O6
O
0.04146 0.03733 0.72718 1 2
  O7
O
0.47756 0.74862 0.10096 1 2
  O8
O
0.21802 0.03879 0.02751 1 2
  O9
O
0.35646 0.05983 0.06059 1 2
  O10
O
0.41027 0.06936 0.76994 1 2
  O11
O
0.98098 0.2239 0.26824 1 2
  O12
O
0.52209 0 0.87034 1 2
  O13
O
0.78806 0.08835 0.5531 1 2
  O14
O
0.12695 0.19108 0.96538 1 2
  O15
O
0.31677 0.27434 0.10354 1 2
  O16
O
0.43941 0.06217 0.95779 1 2
  O17
O
0.07547 0.90735 0.3933 1 2
  O18
O
0.19265 0.04215 0.25818 1 2
  O19
O
0.90875 0.06488 0.10297 1 2
  O20
O
0.65938 0.02252 0.42192 1 2
  O21
O
0.03194 0.28058 0.72145 1 2
  O22
O
0.47997 0.24631 0.10614 1 2
  O23
O
0.30662 0.06147 0.2044 1 2
  O24
O
0.6501 0.20517 0.28485 1 2
  O25
O
0.32112 0.01867 0.38907 1 2
  O26
O
0.2014 0.37678 0.26952 1 2
  O27
O
0.08532 0.1683 0.20009 1 2
  O28
O
0.73228 0.46002 0.29512 1 2
  O29
O
0.22473 0.42377 0.02776 1 2
  O30
O
0.15477 0.47095 0.75439 1 2
  O31
O
0.1152 0.36561 0.0862 1 2
  O32
O
0.07475 0.41488 0.23251 1 2
  O33
O
0.14217 0.52152 0.57669 1 2
  O34
O
0.48952 0.5042 0.12441 1 2
  O35
O
0.36339 0.53877 0.07398 1 2
  O36
O
0.59214 0.41034 0.23703 1 2
  O37
O
0.0361 0.53611 0.74048 1 2
  O38
O
0.20571 0.52464 0.44679 1 2
  O39
O
0.57251 0.42869 0.05093 1 2
  O40
O
0.31176 0.47938 0.2153 1 2
  O41
O
0.06633 0.41387 0.40112 1 2
  O42
O
0.80167 0.27975 0.28821 1 2
  O43
O
0.09916 0.41676 0.89881 1 2
  O44
O
0.66487 0.40284 0.41836 1 2
  O45
O
0.31045 0.26529 0.31988 1 2
  O46
O
0.32317 0.52059 0.40065 1 2
  O47
O
0.6991 0.2356 0.55389 1 2
  O48
O
0.11583 0.67974 0.43133 1 2