Database of Zeolite Structures
 
Framework Type EWE
Powder Diffraction Pattern for EMM-28 calcined
Input Parameters
  Wavelength:  or
  2θ range:
  Step size:
  Polarization factor:
  Background:
  Reference peak is
    peak closest to °2θ
    reflection (hkl)
       scaled to
  Intensity axis:
     
Peak shape
  Pseudo-Voigt: (1-n)Gaussian + n Lorentzian
  FWHM = sqrt (U + V tan θ + W tan2θ)
  Mixing parameter (n): %
  Peak range: FWHM
  Peak width:
    set UVW at: U =   V =   W =
    FWHM =
    FWHM =
  FWHM =
   
Select Output
 
List hkl and intensity
List powder pattern
plot powder pattern
Crystal Data
  Space Group: F m m m   (# 69)   
  Cell parameters: a = 13.7805 Å b = 22.424Å c = 40.101 Å
    α = 90° β = 90° γ = 90 °
  Chemical Formula [Al0.56Si223.44O448]-EWE
  Refinement: 3D Electron diffraction / Rietveld refinement
  Reference: Cichocka, M. O., Burton, A. W., Afeworki, M., Mabon, R., Schmitt, K. D., Strohmaier, K. G., Vroman, H. B., Marella, M. A., Weston, S. C., Zou, X. and Willhammar, T.
Inorg. Chem. , 61, 11103−11109 (2022)
  Atomic Coordinates:          
   
Atom
Form Factor
x
y
z
PP
B(iso)
    
  Si1
Si
0.21 0.1845 0.1552 1 0.4
  Si2
Si
0.1944 0.1231 0.4028 1 0.4
  Si3
Si
0.1902 0.1251 0.283 1 0.4
  Si4
Si
0 0.1949 0.4023 1 0.4
  Si5
Si
0.1118 0 0.3083 1 0.4
  Si6
Si
0.1117 0 0.3844 1 0.4
  Si7
Si
0.2139 0.183 0.0379 1 0.4
  Si8
Si
0 0.2228 0.0378 1 0.4
  Si9
Si
0 0.2217 0.1579 1 0.4
  Si10
Si
0 0.2027 0.2781 1 0.4
  O1
O
0.0954 0.1824 0.1608 1 0.12
  O2
O
0.25 0.25 0.1485 1 0.12
  O3
O
0.258 0.1536 0.1862 1 0.12
  O4
O
0.2257 0.1414 0.1234 1 0.12
  O5
O
0.097 0.1582 0.3974 1 0.12
  O6
O
0.2386 0.1334 0.4395 1 0.12
  O7
O
0.1695 0.0562 0.3996 1 0.12
  O8
O
0.0949 0.1624 0.275 1 0.12
  O9
O
0.25 0.1267 0.25 1 0.12
  O10
O
0.1615 0.0582 0.2922 1 0.12
  O11
O
0 0.2187 0.4401 1 0.12
  O12
O
0 0.2513 0.3784 1 0.12
  O13
O
0 0 0.2996 1 0.12
  O14
O
0.1327 0 0.3464 1 0.12
  O15
O
0 0 0.3932 1 0.12
  O16
O
0.0964 0.1832 0.0423 1 0.12
  O17
O
0.25 0.25 0.0468 1 0.12
  O18
O
0.2426 0.1671 0 1 0.12
  O19
O
0 0.246 0 1 0.12
  O20
O
0 0.2709 0.1854 1 0.12
  O21
O
0 0.25 0.25 1 0.12


Copyright © 2017 Structure Commission of the International Zeolite Association (IZA-SC)