Database of Zeolite Structures
PDF
Download PDF's of
ETL
Tiling
CIF
Download CIF's of
ETL
Framework
H-EU-12, dehydrated
XPD
Calculated pattern
H-EU-12, dehydrated
3D Drawing
ETL
Framework
ETL
Tiling
Materials
ETL
Reference Material
ETL
All materials
Framework
ETL
Framework
ETL
List of T-atoms
ETL
CS and Vertex Symbols
ETL
Accessible Volumes and Areas
ETL
Tiling Arrangement
IZA-SC
All Codes
Intergrowths
Privacy
Terms & Credits
Help
Characteristic Units
CBU's
Chains
Loop configurations
SBU's
Tiles
OSDA's
Home
»
Codes
»
Powder Pattern
Framework Type
ETL
Powder Diffraction Pattern for H-EU-12, dehydrated
Input Parameters
Wavelength:
As specified
CrA1 (2.28970 Å)
CrA2 (2.29361 Å)
Cr (2.29090 Å)
FeA1 (1.93604 Å)
FeA2 (1.93998 Å)
Fe (1.93730 Å)
CuA1 (1.54056 Å)
CuA2 (1.54439 Å)
Cu (1.54180 Å)
MoA1 (0.70930 Å)
MoA2 (0.71359 Å)
Mo (0.71070 Å)
AgA1 (0.55941 Å)
AgA2 (0.56380 Å)
Ag (0.56080 Å)
or
Å
keV
2θ range:
° -
°
Step size:
°2θ
Polarization factor:
Background:
Reference peak is
highest peak in 2θ range
peak closest to
°2θ
reflection (
hkl
)
scaled to
Intensity axis:
-
Peak shape
Pseudo-Voigt: (1-
n
)Gaussian +
n
Lorentzian
FWHM = sqrt (U + V tan θ + W tan
2
θ)
Mixing parameter (
n
):
%
Peak range:
FWHM
Peak width:
set UVW at:
U =
V =
W =
Calculate UVW such that
FWHM =
at
°2θ
FWHM =
at
°2θ
FWHM =
at
°2θ
Select Output
List hkl and intensity
List powder pattern
plot powder pattern
Crystal Data
Space Group:
C m c m
(# 63)
Cell parameters:
a
=
7.4695 Å
b
=
28.8741Å
c
=
17.9156 Å
α =
90°
β =
90°
γ =
90 °
Chemical Formula
[
Si
64.8
Al
7.2
O
144
]
-
ETL
Refinement:
X-ray synchrotron Rietveld refinement, R
wp
=0.075,R
p
=0.057, R
exp
=0.025
Reference:
Bea, J., Cho, J., Lee, J.H., Seo, S.M. and Hong, S.B.
Angew. Chem. Int. Ed.
,
55
, 7369-7373 (2016)
Atomic Coordinates:
Atom
Form Factor
x
y
z
PP
B(iso)
Si1
Si
0.70657
0.45451
0.16337
1
2.93
Si2
Si
0.795
0.26269
0.08465
1
2.93
Si3
Si
0.70596
0.36556
0.06515
1
2.93
Si4
Si
0.5
0.11744
0.05767
1
2.93
Si5
Si
0.5
0.20449
0.16297
1
2.93
Si6
Si
0.5
0.01321
0.08576
1
2.93
O1
O
0.76
0.31678
0.09884
1
3.82
O2
O
0.17663
0.49383
0.12485
1
3.82
O3
O
0.67558
0.23323
0.141
1
3.82
O4
O
0.67629
0.1235
0.00794
1
3.82
O5
O
0.74805
0.40524
0.12581
1
3.82
O6
O
0.5
0.06802
0.09687
1
3.82
O7
O
0.5
0.15608
0.12095
1
3.82
O8
O
1
0.25123
0.10276
1
3.82
O9
O
0.5
0.4672
0.15612
1
3.82
O10
O
0.5
0.36635
0.04191
1
3.82
O11
O
0.5
0.19536
0.25
1
3.82
O12
O
0.7622
0.45156
0.25
1
3.82
O13
O
0.75
0.25
0
1
3.82
O14
O
0.5
0
0
1
3.82
Edit this structure