ITG: XPD Pattern

Framework Type ITG

Powder Diffraction Pattern for edited data of ITQ-38 (calcined)

Modify the data as desired and then press the submit button

Warning: no checking is performed. Please make sure that the data entered are sensible

	Material name
	Original composition	[Si_45.8Ge_10.2O₁₁₂]-ITG
	Edited composition

Space group:		Setting:
Unit cell:	a = Å	b = Å	c = Å
	α = °	β = °	γ = °

Atomic coordinates:

Atom name

Form factor

B(iso)

T1a    Si    0.62729    0.12554    0.2269    0.311    1 
T1b    Ge    0.62729    0.12554    0.2269    0.689    1 
T2a    Si    0.78024    0.12439    0.35939    0.594    1 
T2b    Ge    0.78024    0.12439    0.35939    0.406    1 
T3a    Si    0.97675    0.12857    0.28339    0.488    1 
T3b    Ge    0.97675    0.12857    0.28339    0.512    1 
T4a    Si    0.83193    0.12818    0.15553    0.509    1 
T4b    Ge    0.83193    0.12818    0.15553    0.491    1 
T5a    Si    0.11426    0.37309    0.07016    0.9    1 
T5b    Ge    0.11426    0.37309    0.07016    0.1    1 
T6a    Si    0.26349    0.37812    0.19295    0.954    1 
T6b    Ge    0.26349    0.37812    0.19295    0.046    1 
T7a    Si    0.13633    0.30456    0.2989    1    1 
T8a    Si    0.27616    0.37603    0.42376    1    1 
T9a    Si    0.49754    0.37522    0.37974    1    1 
T10a    Si    0.72773    0.31452    0.43515    0.917    1 
T10b    Ge    0.72773    0.31452    0.43515    0.082    1 
T11    Si    0.81129    0.5    0.36087    1    1 
T12    Si    0.98481    0.5    0.28218    1    1 
T13    Si    0.82852    0.5    0.15485    1    1 
T14    Si    0.65109    0.5    0.2317    1    1 
T15a    Si    0.48994    0.31397    0.23705    0.83    1 
T15b    Ge    0.48994    0.31397    0.23705    0.17    1 
T16a    Si    0.8883    0.3078    0.07268    0.94    1 
T16b    Ge    0.8883    0.3078    0.07268    0.06    1 
O1    O    0.0139    0.30918    0.0876    1    2 
O2    O    0.09643    0.5    0.06921    1    2 
O3    O    0.21171    0.34548    0.12235    1    2 
O4    O    0.24158    0.5    0.20442    1    2 
O5    O    0.38573    0.35493    0.19579    1    2 
O6    O    0.21472    0.30624    0.24503    1    2 
O7    O    0.08658    0.18911    0.30046    1    2 
O8    O    0.05091    0.39377    0.28337    1    2 
O9    O    0.20026    0.32012    0.368    1    2 
O10    O    0.24168    0.33358    0.48977    1    2 
O11    O    0.25143    0.5    0.42138    1    2 
O12    O    0.39791    0.35507    0.41773    1    2 
O13    O    0.47787    0.3145    0.31224    1    2 
O14    O    0.50513    0.5    0.36707    1    2 
O15    O    0.60511    0.33424    0.41716    1    2 
O16    O    0.7586    0.19477    0.42083    1    2 
O17    O    0.79889    0.39254    0.39875    1    2 
O18    O    0.73361    0.5    0.29548    1    2 
O19    O    0.92936    0.5    0.34537    1    2 
O20    O    0.90673    0.5    0.21847    1    2 
O21    O    0.84074    0.39423    0.11579    1    2 
O22    O    0.70962    0.5    0.1688    1    2 
O23    O    0.58312    0.39447    0.22701    1    1 
O24    O    0.52207    0.19872    0.21312    1    2 
O25    O    0.58679    0    0.22621    1    2 
O26    O    0.70945    0.14157    0.172    1    2 
O27    O    0.69269    0.15045    0.29823    1    2 
O28    O    0.76391    0    0.37961    1    2 
O29    O    0.89896    0.14626    0.34033    1    2 
O30    O    0.91531    0.17206    0.21485    1    2 
O31    O    0.85665    0    0.14433    1    2 
O32    O    0.84533    0.19339    0.09015    1    2 
O33    O    0.85615    0.33444    -0.00142    1    2 
O34    O    0    0    0.27514    1    2 
C2    C    0.67612    -0.04524    0.68102    1.297    20 
C3    C    0.74274    0.04003    0.83654    1.511    20 
C4    C    0.08215    -0.09036    0.43185    1.635    20 
C5    C    0.40962    0.3195    0.96708    0.907    5.8 
C6    C    0.55798    0.50003    0.95261    0.19    10 
C7    C    0.38611    0.07868    0.01121    0.734    6.55

Input Profile Parameters

	Wavelength:	or
	2θ range:	° - °
	Step size:	°2θ
	Polarization factor:
	Background:
	Reference peak is	highest peak in 2θ range
		peak closest to °2θ
		reflection (hkl)
	scaled to
	Intensity axis:	-

Peak shape
	Pseudo-Voigt: (1-n)Gaussian + n Lorentzian
	FWHM = sqrt (U + V tan θ + W tan²θ)
	Mixing parameter (n):	%
	Peak range:	FWHM
	Peak width:
		set UVW at:	U = V = W =
		Calculate UVW such that	FWHM = at °2θ
			FWHM = at °2θ
			FWHM = at °2θ

Select Output

List hkl and intensity

List powder pattern

plot powder pattern